Tritan copolyesters are amorphous and have excellent appearance and clarity. The most outstanding features are excellent toughness, hydrolytic stability, and heat and chemical resistance. These new-generation copolyesters can also be molded into various applications without incorporating high levels of residual stress.
Some products contain physical properties that are not displayed in the columns below. To locate the information needed, please choose the product link below. The properties may be found on the datasheet, SDS or sales specification.
| Products | Specific Gravity | Tensile Stress @ Yield | Elongation @ Yield | Tensile Stress @ Break | Elongation @ Break | Flexural Modulus | Izod Impact Strength, Notched | Deflection Temperature | Total Transmittance | Haze | Data Sheet | SDS | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| @ 23°C (73°F) | @ 0.455 MPa (66 psi) | @ 1.82 MPa (264 psi) | |||||||||||
| D 792 | D 638 | ISO 527 | D 638 | D 638 | D 790 | D 256 | D 648 | D 648 | D 1003 | D 1003 | |||
| Tritan Copolyester EX401 | 1.17 | 44 MPa (6400 psi) | 7 % | 53 MPa (7700 psi) | 140 % | 1585 MPa (2.28 x 10^5 psi) | 650 J/m (12.2 ft·lbf/in.) | 109 °C (228 °F) | 92 °C (198 °F) | 92 % | <1 % |  |  |
| Tritan Copolyester TX1000 | 1.18 | 43 MPa (6200 psi) | 7 % | 53 MPa (7700 psi) | 210 % | 1550 MPa (2.25 x 10^5 psi) | 980 J/m (18.4 ft·lbf/in.) | 99 °C (210 °F) | 85 °C (185 °F) | 90 % | <1 % | | |
| Tritan Copolyester TX1001 | 1.18 | 43 MPa (6200 psi) | 7 % | 53 MPa (7700 psi) | 210 % | 1550 MPa (2.25 x 10^5 psi) | 980 J/m (18.4 ft·lbf/in.) | 99 °C (210 °F) | 85 °C (185 °F) | 90 % | <1 % | | |
| Tritan Copolyester TX1800 | 1.18 | 45 MPa (6500 psi) | 7 % | 52 MPa (7600 psi) | 139 % | 1522 MPa (2.2x10^5 psi) | 842 J/m (15.8 ft·lbf/in.) | 101°C (214°F | 85°C (185°F | 91 % | <1 % | | |
| Tritan Copolyester TX1801 - Natural | 1.18 | 45 MPa (6500 psi) | 7 % | 52 MPa (7600 psi) | 139 % | 1522 MPa (2.2x10^5 psi) | 842 J/m (15.8 ft·lbf/in.) | 101°C (214°F | 85°C (185°F | 91 % | <1 % | | |
| Tritan Copolyester TX2000 | 1.17 | 44 MPa (6400 psi) | 7 % | 53 MPa (7700 psi) | 140 % | 1585 MPa (2.28 x 10^5 psi) | 650 J/m (12.2 ft·lbf/in.) | 109 °C (228 °F) | 92 °C (198 °F) | 92 % | <1 % | | |
| Tritan Copolyester TX2001 | 1.17 | 44 MPa (6400 psi) | 7 % | 53 MPa (7700 psi) | 140 % | 1585 MPa (2.28 x 10^5 psi) | 650 J/m (12.2 ft·lbf/in.) | 109 °C (228 °F) | 92 °C (198 °F) | 92 % | <1 % | | |
| Tritan Copolyester TX1500HF | 1.18 | 43 MPa (6200 psi) | 7 % | 52 MPa (7500 psi) | 210 % | 1575 MPa (2.28 x 10^5 psi) | 860 J/m (16.1 ft·lbf/in.) | 94 °C (201 °F) | 81 °C (178 °F) | 91 % | <1 % | | |
| Tritan Copolyester TX1501HF | 1.18 | 43 MPa (6200 psi) | 7 % | 52 MPa (7500 psi) | 210 % | 1575 MPa (2.28 x 10^5 psi) | 860 J/m (16.1 ft·lbf/in.) | 94 °C (201 °F) | 81 °C (178 °F) | 91 % | <1 % | | |